[1]何志明,杨绍斌,常敬华,等.膨润土/聚丙烯酸钠高保水复合材料的研制[J].黑龙江农业科学,2010,(12):124-127.
　HE Zhi-ming,YANG Shao-bin,CHANG Jing-hua,et al.Research on Bentonite/Polyacrylic Acid Sodium Superabsorbent Composite[J].HEILONGJIANG AGRICULTURAL SCIENCES,2010,(12):124-127.
点击复制

膨润土/聚丙烯酸钠高保水复合材料的研制

《黑龙江农业科学》[ISSN:1002-2767/CN:23-1204/S] 卷: 期数: 2010年12 页码: 124-127 栏目: 出版日期: 2010-12-10
Title:
Research on Bentonite/Polyacrylic Acid Sodium Superabsorbent Composite
文章编号:
1002-2767（2010）12-0124-04
作者:
何志明1; 杨绍斌2; 常敬华1; 刘姝杉1
1.辽宁工程技术大学 理学院，辽宁 阜新 123000；
2.辽宁工程技术大学 材料科学与工程学院，辽宁 阜新 123000
Author(s):
HE Zhi-ming1; YANG Shao-bin2; CHANG Jing-hua1; LIU Shu-shan1
1.Science College of Liaoning Technical University，Fuxin，Liaoning 123000；
2.Materials Science and Engineering College of Liaoning Technical University，Fuxin，Liaoning 123000
关键词:
高保水复合材料; 膨润土; 丙烯酸; 吸水性
Keywords:
superabsorbent composite; bentonite; polyacrylic acid; water absorption
分类号:
TQ322.4；TB33
文献标志码:
A
摘要:
以膨润土和丙烯酸为原料，采用溶液聚合法合成膨润土/聚丙烯酸钠高保水复合材料的生产工艺，通过单因素试验和正交试验，确定及优化了该保水复合材料吸水性能的配方，即当膨润土添加量为15 g时，引发剂用量0.9 g、交联剂用量0.03 g、中和度70%、单体用量50 mL（加50 mL蒸馏水稀释）、丙烯酰胺用量15 g。在此配方下制取的复合材料吸水率为164.5，吸盐水率为40.5。该设计生产的复合材料与传统高分子吸水树脂相比，具有聚合反应较易控制、抗盐性好、凝胶强度高等优点，可广泛应用于农林园艺、生态环境治理等领域作保水剂。
Abstract:
Bentonite/polyacrylic acid sodium superabsorbent composite was produced by solution polymerization process using bentonite and propenoic acid.The formula of superabsorbent composite,s water absorption was determined and optimize by single-factor experiment and orthogonal experiment.That was 15 g bentonite，0.9 g initiator，0.03 g cross linking agent，70% neutralization degree，50 mL monomer dosage(dilute by adding 50 mL distilled water)，15 g acrylamide.Thus，the water absorption rate was 164.5 and salt-water absorbency rate was 40.5.Compared with the traditional polymer injectivity resin，the superabsorbent composite had some advantages，such as easily control polymerization reaction，salt resistance，high gel strength，and so on.The product could be widely used as water-retaining agent in forestry gardening，ecological environment，etc.

参考文献/References:

[1]黄杨娥，韩效钊，胡献国.保水剂的研究应用现状与发展[J].安徽化工，2008，34(1):17-20.

[2]杨兰荪.我国膨润土开发应用新成果[J].建材地质，1995（3）:53-60.

[3]林建明，杨正方.膨润土/聚丙烯酸钠盐高吸水性复合材料研究[J].矿物学报，2001，21(3):427-430.


相似文献/References:

[1]何志明,杨绍斌,常敬华,等.玉米淀粉/聚丙烯酸钠高保水复合材料的制备及性能研究[J].黑龙江农业科学,2010,(11):95.
　HE Zhi-ming,YANG Shao-bin,CHANG Jing-hua,et al.Preparation and Performances of Corn Starch/Poly Sodium Acrylate Superabsorbent Polymer Composite Material[J].HEILONGJIANG AGRICULTURAL SCIENCES,2010,(12):95.

备注/Memo

第一作者简介： 何志明（1975-），男，湖北省黄冈市人，学士，讲师，从事矿物加工研究。E-mail:hzm75121@163.com。

更新日期/Last Update: 2014-11-07